Hana ʻia ka pauka kuhili ʻole e ka wai atomization kaʻina a maikaʻi ke kūpaʻa corrosion a me ka lōʻihi.ʻO ka pauka kila kila ka nui o nā hoʻohana ʻoihana.
Hāʻawi i nā ʻano ʻano ʻāpana ʻāpana kila kila me ka nui ʻokoʻa.
1.Hot Isostatic Pressing
2.Metal Injection Molding
Paʻi 3.3D
4. Thermal spraying
1.Water atomization
2.Water kinoea hui atomization
3.Gas atomization
4.Vacuum atomization
Hoʻohui ʻia ka pauda kila % | |||||||||
Papa | Cr | Ni | Mo | Nb | Cu | S | P | C | Si |
303 | 17-19 | 8-13 |
|
|
| 0.15-0.3 | ≤0.2 | ≤0.15 | ≤1 |
304 | 18-20 | 8-12 |
|
|
| ≤0.03 | ≤0.04 | ≤0.08 | ≤1 |
316 | 16-18 | 10-14 | 2-3 |
|
| ≤0.03 | ≤0.04 | ≤0.08 | ≤1 |
303L | 17-19 | 8-13 |
|
|
| 0.15-0.3 | ≤0.2 | ≤0.03 | ≤1 |
304L | 18-20 | 8-12 |
|
|
| ≤0.03 | ≤0.04 | ≤0.03 | ≤1 |
316L | 16-18 | 10-14 |
|
|
| ≤0.03 | ≤0.04 | ≤0.03 | ≤1 |
317L | 18-21 | 12-16 | 3-4 |
|
| ≤0.03 | ≤0.04 | ≤0.03 | ≤1 |
314 | 24-27 | 18-21 |
|
|
| ≤0.03 | ≤0.04 | ≤0.2 | 1.5/2.5 |
310 | 24-26 | 19-22 |
|
|
| ≤0.03 | ≤0.04 | ≤0.08 | ≤1 |
303LSC | 17-19 | 8-13 |
|
| 2 | 0.15-0.3 | ≤0.2 | ≤0.03 | ≤1 |
304LSC | 17-19 | 8-13 |
|
| 2 | ≤0.03 | ≤0.04 | ≤0.03 | ≤1 |
316LSC | 16-19 | 10-14 | 2-3 |
| 2 | ≤0.03 | ≤0.04 | ≤0.03 | ≤1 |
410L | 11.5-13.5 |
|
|
|
| ≤0.03 | ≤0.04 | ≤0.03 | ≤1 |
430L | 16-18 |
|
|
|
| ≤0.03 | ≤0.04 | ≤0.03 | ≤1 |
434L | 16-18 |
| 0.75-1.25 |
|
| ≤0.03 | ≤0.04 | ≤0.08 | ≤1 |
434LNB | 16-18 |
| 0.75-1.25 | 0.4-0.6 |
| ≤0.03 | ≤0.04 | ≤0.03 | ≤1 |
410 | 11.5-13.5 |
|
|
|
| ≤0.03 | ≤0.04 | ≤0.25 | ≤1 |
420 | 12-14 |
|
|
|
| ≤0.03 | ≤0.04 | 0.25/0.35 | ≤1 |
430 | 16-18 |
|
|
|
| ≤0.03 | ≤0.04 | ≤0.08 | ≤1 |
434 | 16-18 |
| 0.75-1.25 |
|
| ≤0.03 | ≤0.04 | ≤0.08 | ≤1 |
440 | 16-18 |
|
|
|
| ≤0.03 | ≤0.04 | 0.9/1.2 | ≤1 |
17-4PH | 15-17.5 | 3-5 |
| 0.15-0.456 | 3-5 | ≤0.03 | ≤0.04 | ≤0.07 | ≤1 |
15-5PH | 14-15.5 | 3.5-5.5 |
|
| 2.5-4.5 | ≤0.03 | ≤0.04 | <=0.07 | ≤1 |
Hiki ke hoʻohana ʻia ka pauka kila kila no ka hoʻoheheʻe ʻana i ka wela, ka pauka metallurgy, ka pauka metallurgy press sintering (PM), injection molding (MIM) sintering filter, etc., water atomization oxygen content<4000PPM, hoʻokuʻu kinoea<1000PPM.
●Even pauda haku mele, emi haumia
● sphericity kiʻekiʻe
● Haʻahaʻa oxygen maʻiʻo
●Maikaʻi flowability
●Kiʻekiʻe hoʻokuʻu haʻahaʻa, kiʻekiʻe piula wai
●Ka pauda hollow emi, emi iho ka pauda satellite
1.Huarui i koʻikoʻi hoʻokele waiwai.Ho'āʻo mua mākou i kā mākou huahana ma hope o ka hoʻopau ʻana i kā mākou hana, a hoʻāʻo hou mākou ma mua o kēlā me kēia lawe ʻana, ʻo ia hoʻi ka laʻana.A inā makemake ʻoe, makemake mākou e ʻae i ka ʻaoʻao ʻekolu e hoʻāʻo.ʻOiaʻiʻo inā makemake ʻoe, hiki iā mākou ke hāʻawi i kahi laʻana iā ʻoe e hoʻāʻo.
2. ʻO ka maikaʻi o kā mākou huahana e hōʻoia ʻia e Sichuan Metallurgical Institute a me Guangzhou Institute of Metal Research.Hiki i ka hui lōʻihi me lākou ke mālama i ka manawa hoʻāʻo nui no nā mea kūʻai aku.